Zipangizo Zitsulo

Kufotokozera Kwachidule:

Zitsulo zopangira zitsulo ndizitsulo zomwe zimachepetsedwa kukhala tinthu tating'onoting'ono ndipo ndizoyambira zoyambira pazinthu zambiri zosindikiza za 3D zomwe zimapanga magawo azitsulo. Kusindikiza kwa 3D, kotchedwanso kuti zowonjezera zowonjezera (AM), ndikupanga magawo ndi zinthu mosanjikiza. Makhalidwe onse a ufa wachitsulo ndi mtundu wa makina osindikizira a 3D amadziwika ndi zomwe zimatha kumapeto. Makhalidwe a ufa amachitika kutengera momwe amapangidwira, zomwe zimatha kubweretsa kusiyanasiyana kwakapangidwe kazinthu ndi kuyera.


Mankhwala Mwatsatanetsatane

Zogulitsa

Zosapanga dzimbiri zitsulo, Mtundu ; 316L
Makhalidwe Athupi kukula kwa tinthu 15-53 μm
Mawonekedwe Ozungulira
kutuluka 40 S (Kuyenda kwa mita)
kuwoneka kachulukidwe 3.9 g / cm3
Kuchulukitsitsa 7.98 g / cm3
Kupangidwa kwa Mankhwala Fe Chotsalira
Kr 16 ~ 18%%
Ndi 10 ~ 14 wt%
Mo 2 ~ 3 wt%
Mn ≤2 wt%
Si W1 wt%
C ≤0.05 wt%
P ≤0.045 wt%
S ≤0.03 wt%
O ≤0.1 wt%
Mbali katundu Kachulukidwe wachibale Pafupifupi. 99.9%
Kulimba kwamakokedwe Pafupifupi. 560 MPa
Perekani mphamvu Pafupifupi. 480 MPa
Kutalika pambuyo pa kusweka Pafupifupi. 20%
Kutanuka modulus Pafupifupi. 180 GPa
Kuuma Pafupifupi. 85 HRB (158 HB)
Zotayidwa aloyi , Mtundu: AlSi10Mg
Makhalidwe Athupi kukula kwa tinthu 15-53 μm
Mawonekedwe Ozungulira
kutuluka 150 S (Kuyenda kwa mita)
kuwoneka kachulukidwe 1.45 g / cm3
Kuchulukitsitsa 2.67 g / cm3
Kupangidwa kwa Mankhwala Al Chotsalira
Si 9 ~ 10 wt%
Mg 0.2 ~ 0.45 wt%
Cu ≤0.05 wt%
Mn ≤0.45 wt%
Ndi ≤0.05 wt%
Fe ≤0.55 wt%
Ti ≤0.15 wt%
C 0.0075wt%
Mbali katundu Kachulukidwe wachibale ≥95%
Kulimba kwamakokedwe Pafupifupi. 330 MPa
Perekani mphamvu Pafupifupi. 245 MPa
Kutalika pambuyo pa kusweka Pafupifupi. 6%
Kutanuka modulus Pafupifupi. 70 GPa
Kuuma Pafupifupi. 120 HB

 

 Aloyi titaniyamu , Mtundu: TC4 (Ti-6Al-4V)
Makhalidwe Athupi kukula kwa tinthu 15-45 μm
Mawonekedwe Ozungulira
kutuluka 45 S (mita yoyendera Hall)
kuwoneka kachulukidwe 2.5 g / cm3
Kuchulukitsitsa 4.51 g / cm3
Kupangidwa kwa Mankhwala Ti Chotsalira
Al 5 ~ 6.75 wt%
V 3.5 ~ 4.5 wt%
Fe ≤0.25 wt%
C ≤0.02 wt%
Y 0.005 wt%
O 0.14 ~ 0.16 wt%
N ≤0.02 wt%
Cu ≤0.1 wt%
Zina 0,4%
Mbali katundu Kachulukidwe wachibale Pafupifupi 99.9%
Kulimba kwamakokedwe Pafupifupi. 1000 MPa
Perekani mphamvu Pafupifupi 900 MPa
Kutalika pambuyo pa kusweka Pafupifupi. 10%
Kutanuka modulus Pafupifupi 110 GPa
Kuuma Pafupifupi. 300 HV (294 HB)

 

Faifi tambala-m'munsi superalloy Mtundu: IN718
Makhalidwe Athupi kukula kwa tinthu 15-53 μm
Mawonekedwe Ozungulira
kutuluka 40 S (Kuyenda kwa mita)
kuwoneka kachulukidwe 4.1 g / cm3
Kuchulukitsitsa 8.15 g / cm3
Kupangidwa kwa Mankhwala Ndi 50 ~ 55 wt%
Kr 17 ~ 22 wt%
Nb 4.75 ~ 5.5 wt%
Mo 2.8, 3.3 wt%
Kampaniyo Co W1 wt%
C ≤0.08 wt%
P ≤0.015 wt%
Si 0.35 wt%
Al 0.2 ~ 0.8 wt%
Ti 0,65 ~ 1,15 wt%
Fe Chotsalira
Mbali katundu Kachulukidwe wachibale ≥99%
Kulimba kwamakokedwe Pafupifupi. 980 MPa (1240 MPa atalandira chithandizo cha kutentha)
Perekani mphamvu Pafupifupi. 780 MPa (1000 MPa atalandira chithandizo cha kutentha)
Kutalika pambuyo pa kusweka 12 ~ 30%
Kutanuka modulus Pafupifupi. 160 GPa
Kuuma Pafupifupi. 30 HRC (47 HRC mutalandira chithandizo chakutentha)

 

Zitsulo Zamadzimadzi, Mtundu: MS1
Makhalidwe Athupi kukula kwa tinthu 15-53 μm
Mawonekedwe Ozungulira
kutuluka 40 S (Kuyenda kwa mita)
kuwoneka kachulukidwe 4.3 g / cm3
Kuchulukitsitsa 8 g / cm3
Kupangidwa kwa Mankhwala Fe Chotsalira
Kampaniyo Co 8.5 ~ 9.5 wt%
Ndi 17 ~ 19 wt%
Mo 4.2 ~ 5.2 wt%
Mn ≤0.1 wt%
Ti 0.6 ~ 0.8 wt%
C ≤0.03 wt%
Al 0.05, 0.15 wt%
S ≤0.01 wt%
Kr ≤0.3 wt%
Mbali katundu Kachulukidwe wachibale ≥99%
Kulimba kwamakokedwe Arrpox. 900 MPa (1930 MPa pambuyo pochiritsidwa ndi kutentha)
Perekani mphamvu Arrpox. 1000 MPa (1890 MPa pambuyo pochizira kutentha)
Kutalika pambuyo pa kusweka Arrpox. 4%
Kutanuka modulus Arrpox. 160 GPa (180 GPa pambuyo pochizira kutentha)
Kuuma Arrpox. 35 HRC
 Cobalt-chromium aloyi, Mtundu: MP1 (CoCr-2Lc)
Makhalidwe Athupi kukula kwa tinthu 15-53 μm
Mawonekedwe Ozungulira
kutuluka 40 S (Kuyenda kwa mita)
kuwoneka kachulukidwe 4.1 g / cm3
Kuchulukitsitsa 8.3 g / cm3
Kupangidwa kwa Mankhwala Kampaniyo Co Chotsalira
Kr 26 ~ 30 wt%
Mo 5 ~ 7 wt%
Si W1 wt%
Mn W1 wt%
Fe ≤0.75 wt%
C ≤0.16 wt%
Ndi ≤0.1 wt%
Mbali katundu Kachulukidwe wachibale ≥99%
Kulimba kwamakokedwe Pafupifupi 100 MPa
Perekani mphamvu Pafupifupi 900 MPa
Kutalika pambuyo pa kusweka Pafupifupi. 10%
Kutanuka modulus Pafupifupi. 200 GPa
Kuuma 35 ~ 45 HRC (323 ~ 428 HB)

 